Structure and optical properties of thin poly(p-xylylene) - Silver nanocomposite films prepared by low-temperature vapor deposition polymerizationстатья
Статья опубликована в высокорейтинговом журнале
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 19 сентября 2015 г.
Аннотация:In this study, variable-temperature grazing-incidence X-ray diffraction, transmission electron and scanning force microscopy were employed to address the semicrystalline structure and surface morphology of thin poly(p-xylylene) - silver nanocomposite films with Ag concentrations up to 12 vol.%. It was observed that the dominant crystalline modification of poly(p-xylylene) in the studied films is alpha-form, which is in contrast to thick poly(p-xylylene) films deposited at liquid nitrogen temperature where beta-form prevails. The films exhibit planar texture that can be further enhanced on annealing. The optical properties of the films were studied by UV-vis and IR-spectroscopy. It was found that the samples display surface plasmon resonance, with the peak wavelength in the range of 435-445 nm. The peak positions undergo a redshift upon a long-term storage under ambient conditions. The IR-spectroscopy reveals the bands, which can be assigned to the vibrations of oxygen-containing groups, with intensity increasing with silver content. (C) 2015 Elsevier Ltd. All rights reserved.