ITER-grade tungsten limiters damage under high turbulent heat flux in the T-10 tokamak

Grashin, S.A.; Arkhipov, I.I.; Budaev, V.P.; Karpov, A.V.; Klyuchnikov, L.A.; Khimchenko, L.N.; Melnikov, A.V.; Sarychev, D.V.; Sergeev, N.S.; Zemtsov, I.A.

Авторы: Grashin S.A., Arkhipov I.I., Budaev V.P., Karpov A.V., Klyuchnikov L.A., Khimchenko L.N., Melnikov A.V., Sarychev D.V., Sergeev N.S., Zemtsov I.A.
Журнал: Fusion Engineering and Design
Том: 146
Номер: Part В
Год издания: 2019
Издательство: Elsevier BV
Местоположение издательства: Netherlands
Первая страница: 2100
Последняя страница: 2104
DOI: 10.1016/j.fusengdes.2019.03.115
Аннотация: Tungsten is foreseen as plasma facing material for ITER. The tungsten testing under high heat loads is very important for ITER operation prediction. In a real tokamak conditions combination of the heat and particle fluxes could enhance tungsten destruction and erosion. Some mechanisms of plasma-surface interaction can lead to a concentration of heat flux onto the small zones of the divertor and limitersand cause a damage or melting of tungsten. One of such mechanisms could be non-ambipolar flow toward the tungsten surface due to the arcs and sparks.This report presents the results of the tungsten limiters analysis in the T-10 tokamak after 2015-2017 experimental campaigns. The limiters were made from the ITER-grade WMP “POLEMA” tungsten. Significant cracking of the tungsten limiter surface was observed. Heat load up to 2 MW /m2 lead to the micro-cracks (1-2 µm wide) development at the grain borders accompanied by the destruction of the surface. On the inner board of the torusheat flux to the edge of the limiter ring can exceed 5 MW m-2during the ECR heating.In such discharges, the tungsten plates at the inboard of the vessel were heated to temperature exceeded 20000C.Local thermal load of more than 40 MW/m2 leads to tungsten surface melting. Intensive sparking and arcing, deep cracks and edge melting were observed on the tungsten tiles after the experimental campaigns. In these zones macro cracks developed with a width up to 100µm and lengths of 5-50 mm. It is supposing that the nonambipolar flow due to the arcs and sparks leads to the observed overheating, cracking and melting of the tungsten surface. In the T-10 tokamak edge plasma conditions strong of the ITER-grade tungsten limiters was observed during the experimental campaigns.
Добавил в систему: Архипов Игорь Иванович

	ИСТИНА	Войти в систему Регистрация
	ИСТИНА ЦЭМИ РАН
	Главная Поиск Статистика О проекте Помощь

ИСТИНА

ИСТИНА ЦЭМИ РАН

ITER-grade tungsten limiters damage under high turbulent heat flux in the T-10 tokamakстатья