Growth from the Melt and Properties Investigation of ScF3 Single Crystalsстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 3 октября 2019 г.
Аннотация:ScF3 optical quality bulk crystals of the ReO3 structure type (space group Pm3¯m, a = 4.01401(3) Å) have been grown from the melt by Bridgman technique, in fluorinating atmosphere for the first time. Aiming to substantially reduce vaporization losses during the growth process graphite crucibles were designed. The crystal quality, optical, mechanical, thermal and electrophysical properties were studied. Novel ScF3 crystals refer to the low-refractive-index (nD = 1.400(1)) optical materials with high transparency in the visible and IR spectral region up to 8.7 µm. The Vickers hardness of ScF3 (HV ~ 2.6 GPa) is substantially higher than that of CaF2 and LaF3 crystals. ScF3 crystals possess unique high thermal conductivity (k = 9.6 Wm−1К−1 at 300 K) and low ionic conductivity (σ = 4 × 10−8 Scm−1 at 673 К) cause to the structural defects in the fluorine sublattice.