The influence of nitrogen doping on the adsorption of organic solvent vapors by carbon nanotubes and few-layer graphene nanoflakesтезисы доклада Тезисы
- Авторы: Stepan Kupreenko, Natalia Strokova
- Сборник: 21st Romanian International Conference on Chemistry and Chemical Engineering
- Тезисы
- Год издания: 2019
- Место издания: Romania
- Первая страница: S6-116
- Последняя страница: S6-116
- Аннотация: Carbon nanomaterials are widely used for adsorption of organic pollutants [1]. They have high specific surface area and adsorption capacity. Variation of synthesis conditions allow to control the pore size distribution. The presence of certain functional groups on surface can stimulate the adsorption of certain solvents vapors. This work focuses on the influence of nitrogen doping on adsorption characteristics of carbon nanotubes (CNT) and few-layer graphene nanoflakes (GNF). Carbon nanomaterials were obtained by pyrolitic decomposition of hexane (for pristine materials) / acetonitrile (for N-doped materials) on a mesoporous oxide catalyst. Vapor sorption of acetone, ethyl acetate, toluene and acetic acid on doped and pristine materials was investigated. Using the BET method, specific surface area S values were determined. They are in agreement with data of low temperature nitrogen adsorption. Few-layer graphene nanoflakes demonstrate the highest value of S (1400 m2/g). Next is N-doped analogue (400 m2/g), then N-CNT (260 m2/g) and finally CNT (160 m2/g). Using measurements at two temperatures (20 and 30 °C), values of isosteric heat of sorption Qst were obtained. It was found that few-layer graphene nanoflakes are more preferable for adsorption of polar solvents, because heat of sorption for selected adsorbates increases with an increase in their dipole moment from 35 to 39 kJ/mol. N-doped materials proved to be best sorbents for acetic acid due to the basic properties of functional groups and chemical bonding between molecules of adsorbate and adsorbent. The highest values of heat of adsorption were obtained for N-CNT (Qst = 41 kJ/mol) and NGNF (Qst = 49 kJ/mol). Acknowledgments This work was funded by RFBR according to the research project № 18-33-00322. References 1. Zhang X., Gao B., Creamer A. E., Cao C., Li Y., Adsorption of VOCs onto engineered carbon materials: A review. A Journal of Hazardous Materials, 2017. 338, 102-123.
- Добавил в систему: Купреенко Степан Юрьевич
Прикрепленные файлы
| № | Имя | Описание | Имя файла | Размер | Добавлен |
|---|---|---|---|---|---|
| 1. | Краткий текст | Тезисы доклада | S6_117.pdf | 68,6 КБ | 5 ноября 2019 [KupreenkoSU] |