Аннотация:Abstract. The simulation of results of the tests of tubular samples (which are made of copper) at 250°C is conducted. These tests were published by S. Murakami, Y. Sanomura and K. Saitoh in 1986. On these samples constant axial stress and shear stress, which once or cyclically changed sign, simultaneously were acted. In the description of experimental data a vector damage parameter with piecewise-constant rate of damage accumulation is used. In this article two versions of kinetic equations, proposed by L. M. Kachanov, and in addition the variant of the system of kinetic equations, proposed by I. V. Namestnikova and S. A. Shesterikov, is considered. The good agreement between the experimental and theoretical values of times to failure is received.
Key words: creep rupture, non-stationary complex stress state, tubular specimens, failure time, kinetic theory, damage, vector parameter.
Аннотация. Проведено моделирование результатов испытаний трубчатых образцов из меди при 250°С, опубликованных S.Murakami, Y. Sanomura и K. Saitoh в 1986 г. В данных испытаниях на длительную прочность в образцах одновременно действовали постоянное осевое напряжение и касательное напряжение, которое однократно или циклически меняло знак. При описании экспериментальных данных используется векторный параметр поврежденности с кусочно-постоянной скоростью накопления повреждений. В данной статье используются два варианта кинетических уравнений, предложенные Л.М. Качановым, и дополнительно вариант системы кинетических уравнений, предложенной И.В. Наместниковой и С.А. Шестериковым. Получено хорошее соответствие экспериментальных и теоретических значений времен до разрушения.
Ключевые слова: длительная прочность, нестационарное сложное напряженное состояние, трубчатые образцы, время до разрушения, кинетическая теория, поврежденность, векторный параметр.