Аннотация:Spectra of spin current in a heterostructure, consisting of an epitaxial film of yttrium iron garnetY3Fe5O12 (YIG), grown on a gadolinium gallium garnet Gd3Ga5O12 (GGG) substrate, and a platinum (Pt)film, have been investigated. The spin current, induced by microwave irradiation of the YIG film in the fer-romagnetic-resonance mode and by the inverse spin Hall effect, was measured in the temperature rangeT= 77–300 K at the microwave power and frequency varied in the ranges of 20 μW–50 mW and 2–9 GHz,respectively, to determine the inf luence of spin-wave resonances in YIG on the spectral characteristics of thespin current. It is found that the spin current amplitude due to spin-wave resonances of surface spin wavesbecomes comparable to the contribution from the ferromagnetic resonance with an increase in the microwavepower at frequencies f = 2–3 GHz.